| 75 kg/m鋼軌鋁熱焊接頭斷裂失效研究(51 卷) |
| 英文標題 |
| Study on fracture failure of 75 kg/m rail weld by thermit welding |
| 摘要 |
| 2010年下半年75 kg/m PG4淬火軌鋁熱焊斷裂接頭部分出現(xiàn)了同一形式的斷裂方式。本文通過宏觀斷口形貌、斷口掃描電鏡分析、裂紋源及擴展區(qū)域金相觀察，以及力學性能測定等手段對斷裂接頭進行失效分析。分析認為，斷裂接頭的起裂位置是在軌頭下顎與焊筋邊緣相交處，通過疲勞裂紋 |